Future is capable of producing PMI foam core whose quality is equivalent to Rohachell, the fishing float bodies were made by Future produced PMI foam and machined by our own CNC machining facility. These bodies are made by IGF110, and cut to different shapes by customers drawing, good cell structure makes fishing and painting more easier.
| Uses | Float body making PMI foam |
| Density | 100kg/m³ |
| Closed cell rate | 98% |
| CNC service | Drilling, cutting, toolling |
| Shapes | Diamond, eye drop, power pencil and etc.. |
| Regular size | 4x8mm, 4x10mm, 4x12mm, 4x14mm, 4x16mm, 4x18mm |
The available shapes of fishing body:
PMI foam specification:
| Mechanical properties at room temperature | Medium temperature 130℃ performance | |||||||||||||||
| Density (kg/m³) |
Model | Compressive strength | Compression modulus | Tensile Strength | Tensile modulus | Elongation at break | Shear strength | Shear modulus | Bending strength | Flexural modulus | Deflection | Compressive strength | Compression modulus | Rate of dimensional change | ||
| Mpa | Mpa | Mpa | Mpa | % | Mpa | Mpa | Mpa | Mpa | mm | Mpa | Mpa | Length*width*height (Ratio%） |
||||
| Testing standard | GB/T 8813-2008 | GB/T 9641-1988 | GB/T 1455-2008 | GB/T 8812.2-2007 | GB/T 8813-2008 | GB/T 8811-2008 | ||||||||||
| 52 | FXK52 | 1 | 46 | 1.5 | 80 | 3.1 | 0.8 | 26 | 2.2 | 72 | 26 | 0.6 | 28 | 0.1 | 0.1 | 0.32 |
| 75 | FXK75 | 1.8 | 79 | 2.7 | 100 | 3.2 | 1.2 | 35 | 2.7 | 84 | 29 | 1.1 | 48 | 0.23 | 0.25 | 0.49 |
| 110 | FXK110 | 3.3 | 141 | 4.6 | 178 | 3 | 2.3 | 66 | — | — | — | 2.1 | 85 | 0.12 | 0.22 | 0.8 |