PMI Foam 110 Square Bar 450mm for Fishing Float Body

Brand: Fucell®

Material: PMI foam

Color: Natural white

Density: 110kg/m3

Closed cell rate: 98%

CNC service: Cutting/drilling/shaping

Uses: Fishing pole making

Fishing type: Coarse/fly/freshwater/ice fishing

Product Description

Specifications

Product Description

Advantages of Fucell® PMI foam:
1. Large buoyancy ratio.
2. Low water absorption
3. Uniform and stable density.
4. Strong and durable material.
5. Easy to be CNC machined.

Recommended model number: FF110 which is similar with Rohachell 110 performance, which is perfect for sea fishing, FF51 and FF71 are also recommended for fishing float making.

Comes in three regular sizes:
Future composites offers PMI CNC service, with high cutting precision and low material loss. For other size, please contact our sales person for best price.

Side length	Length
10*10mm	450mm
15*15mm	450mm
20*20mm	450mm

Please follow the specification and contact us for more information.

Density (kg/m³)	Model	Mechanical properties at room temperature											Medium temperature 130℃ performance
		Compressive strength	Compression modulus	Tensile Strength	Tensile modulus	Elongation at break	Shear strength	Shear modulus	Bending strength	Flexural modulus	Deflection	Closed cell rate	Compressive strength	Compression modulus	Rate of dimensional change
		Mpa	Mpa	Mpa	Mpa	%	Mpa	Mpa	Mpa	Mpa	mm	%	Mpa	Mpa	Lengthwidthheight (Ratio%）
Testing standard		GB/T 8813-2008		GB/T 9641-1988			GB/T 1455-2008		GB/T 8812.2-2007			GB/T 10799-2008	GB/T 8813-2008		GB/T 8811-2008
32	FF32	0.32	14	0.66	28	3.8	0.28	7.6	0.86	31	22	99	0.27	11	0.22	0.2	0.46
	FU30	0.42	20	0.56	39	0.69	—	—	1	31	30	—	0.35	16	0.22	0.23	0.49
40	FC40	0.6	34	0.9	54	1.7	0.4	19	1.3	55	15	—	0.4	17	—	—	—
	FU40	0.72	29	1.2	51	3.4	—	—	1.7	58	33	—	0.52	24	0.22	0.24	0.59
52	FC52	0.9	41	1.2	73	1.9	0.73	27	1.6	70	19	99	0.62	28	0.15	0.15	0.32
	FM52	0.9	51	1.3	81	1.2	1	26	1.5	65	15	97	0.5	24	0.2	0.2	0.34
	FF52	1	43	1.5	77	3.1	0.9	24	2.1	76	22	99	0.6	27	0.28	0.3	0.46
75	FC72	1.4	59	1.8	101	2.3	1.2	40	2	92	13	99	0.9	43	0.21	0.22	0.35
	FF75	1.8	72	2.4	113	3.6	1.6	45	3.4	117	20	98	1.1	49	0.2	0.16	0.48
	FU75	1.7	75	2.2	89	3.8	1.2	37	3.3	105	23	—	1.1	48	0.19	0.24	0.33
110	FF110	3.2	138	3.9	200	2.7	2	63	5.5	195	19	98	1.7	77	0.19	0.19	0.4
	FU110	2.2	93	3.3	160	3.6	2.2	63	4.5	143	21	—	1.4	62	0.23	0.21	0.48
200	FF200	8.5	317	7.5	410	2.4	—	—	13	449	22	99	3.8	141	0.44	0.41	0.54

Photo of PMI Core For Making Pole Fishing Float Bodies Similar Rohacell IG110

The CNC shapes of PMI float body:

Specifications

Please follow the specification and contact us for more information.

Density (kg/m³)	Model	Mechanical properties at room temperature											Medium temperature 130℃ performance
		Compressive strength	Compression modulus	Tensile Strength	Tensile modulus	Elongation at break	Shear strength	Shear modulus	Bending strength	Flexural modulus	Deflection	Closed cell rate	Compressive strength	Compression modulus	Rate of dimensional change
		Mpa	Mpa	Mpa	Mpa	%	Mpa	Mpa	Mpa	Mpa	mm	%	Mpa	Mpa	Lengthwidthheight (Ratio%）
Testing standard		GB/T 8813-2008		GB/T 9641-1988			GB/T 1455-2008		GB/T 8812.2-2007			GB/T 10799-2008	GB/T 8813-2008		GB/T 8811-2008
32	FF32	0.32	14	0.66	28	3.8	0.28	7.6	0.86	31	22	99	0.27	11	0.22	0.2	0.46
	FU30	0.42	20	0.56	39	0.69	—	—	1	31	30	—	0.35	16	0.22	0.23	0.49
40	FC40	0.6	34	0.9	54	1.7	0.4	19	1.3	55	15	—	0.4	17	—	—	—
	FU40	0.72	29	1.2	51	3.4	—	—	1.7	58	33	—	0.52	24	0.22	0.24	0.59
52	FC52	0.9	41	1.2	73	1.9	0.73	27	1.6	70	19	99	0.62	28	0.15	0.15	0.32
	FM52	0.9	51	1.3	81	1.2	1	26	1.5	65	15	97	0.5	24	0.2	0.2	0.34
	FF52	1	43	1.5	77	3.1	0.9	24	2.1	76	22	99	0.6	27	0.28	0.3	0.46
75	FC72	1.4	59	1.8	101	2.3	1.2	40	2	92	13	99	0.9	43	0.21	0.22	0.35
	FF75	1.8	72	2.4	113	3.6	1.6	45	3.4	117	20	98	1.1	49	0.2	0.16	0.48
	FU75	1.7	75	2.2	89	3.8	1.2	37	3.3	105	23	—	1.1	48	0.19	0.24	0.33
110	FF110	3.2	138	3.9	200	2.7	2	63	5.5	195	19	98	1.7	77	0.19	0.19	0.4
	FU110	2.2	93	3.3	160	3.6	2.2	63	4.5	143	21	—	1.4	62	0.23	0.21	0.48
200	FF200	8.5	317	7.5	410	2.4	—	—	13	449	22	99	3.8	141	0.44	0.41	0.54