1mm 2mm PMI Foam Core IG51 IG71 for UAV Helicopter China Factory

Origin: Guangdong, China

Brand: Fucell®

Material: Polymethacrylimide (pmi) foam

Color: White

Density: 52kg/m3, 75kg/m3

Width: 1220mm

Thickness: 0.5-100mm

Uses: UAV, helicopter

Product Description

Specifications

Product Description

High Strength PMI Structural Foam advanced foam is mainly applied in the fields of aviation & aerospace, such as fairing and middle section of launch vehicle. Because of excellent properties, it can also be used in back pressure frame of large civil plane.
Fire retardant PMI Foam Manufacturer is mainly used in main & tail rotor blades and fuselage panels,etc of helicopters.

As one of the products that use the most carbon fiber materials, unmanned aircraft, Future can provide a series of carbon fiber products:

1, carbon fiber fabric;

2, carbon fiber tube;

3, carbon fiber rod;

4, carbon fiber mold pressing parts;

5, PMI foam core.

Please send email to our sales person for the products you need, we could offer for low MOQ with best price.

Advantages of 1mm 2mm PMI foam IG51 71 core for UAV helicopter:

Different PMI foam core density:

CNC cutting for different size and shape:

Specifications

PMI form core properties:

Density (kg/m³)	Model	Mechanical properties at room temperature											Medium temperature 130℃ performance
		Compressive strength	Compression modulus	Tensile Strength	Tensile modulus	Elongation at break	Shear strength	Shear modulus	Bending strength	Flexural modulus	Deflection	Closed cell rate	Compressive strength	Compression modulus	Rate of dimensional change
		Mpa	Mpa	Mpa	Mpa	%	Mpa	Mpa	Mpa	Mpa	mm	%	Mpa	Mpa	Lengthwidthheight (Ratio%）
Testing standard		GB/T 8813-2008		GB/T 9641-1988			GB/T 1455-2008		GB/T 8812.2-2007			GB/T 10799-2008	GB/T 8813-2008		GB/T 8811-2008
32	FF32	0.32	14	0.66	28	3.8	0.28	7.6	0.86	31	22	99	0.27	11	0.22	0.2	0.46
32	FU30	0.42	20	0.56	39	0.69	—	—	1	31	30	—	0.35	16	0.22	0.23	0.49
40	FC40	0.6	34	0.9	54	1.7	0.4	19	1.3	55	15	—	0.4	17	—	—	—
40	FU40	0.72	29	1.2	51	3.4	—	—	1.7	58	33	—	0.52	24	0.22	0.24	0.59
52	FC52	0.9	41	1.2	73	1.9	0.73	27	1.6	70	19	99	0.62	28	0.15	0.15	0.32
	FM52	0.9	51	1.3	81	1.2	1	26	1.5	65	15	97	0.5	24	0.2	0.2	0.34
	FF52	1	43	1.5	77	3.1	0.9	24	2.1	76	22	99	0.6	27	0.28	0.3	0.46
75	FC72	1.4	59	1.8	101	2.3	1.2	40	2	92	13	99	0.9	43	0.21	0.22	0.35
	FF75	1.8	72	2.4	113	3.6	1.6	45	3.4	117	20	98	1.1	49	0.2	0.16	0.48
	FU75	1.7	75	2.2	89	3.8	1.2	37	3.3	105	23	—	1.1	48	0.19	0.24	0.33
110	FF110	3.2	138	3.9	200	2.7	2	63	5.5	195	19	98	1.7	77	0.19	0.19	0.4
110	FU110	2.2	93	3.3	160	3.6	2.2	63	4.5	143	21	—	1.4	62	0.23	0.21	0.48
200	FF200	8.5	317	7.5	410	2.4	—	—	13	449	22	99	3.8	141	0.44	0.41	0.54