1mm 2mm PMI Foam Core IG51 IG71 for UAV Helicopter China Factory
Origin: Guangdong, China
Brand: Fucell®
Material: Polymethacrylimide (pmi) foam
Color: White
Density: 52kg/m3, 75kg/m3
Width: 1220mm
Thickness: 0.5-100mm
Uses: UAV, helicopter
Product Description
High Strength PMI Structural Foam advanced foam is mainly applied in the fields of aviation & aerospace, such as fairing and middle section of launch vehicle. Because of excellent properties, it can also be used in back pressure frame of large civil plane.
Fire retardant PMI Foam Manufacturer is mainly used in main & tail rotor blades and fuselage panels,etc of helicopters.
As one of the products that use the most carbon fiber materials, unmanned aircraft, Future can provide a series of carbon fiber products:
1, carbon fiber fabric;
2, carbon fiber tube;
3, carbon fiber rod;
4, carbon fiber mold pressing parts;
5, PMI foam core.
Please send email to our sales person for the products you need, we could offer for low MOQ with best price.
PMI form core properties:
Density | Model | Mechanical properties at room temperature | Medium temperature 130℃ performance | ||||||||||||||
Compressive strength | Compression modulus | Tensile Strength | Tensile modulus | Elongation at break | Shear strength | Shear modulus | Bending strength | Flexural modulus | Deflection | Closed cell rate | Compressive strength | Compression modulus | Rate of dimensional change | ||||
Mpa | Mpa | Mpa | Mpa | % | Mpa | Mpa | Mpa | Mpa | mm | % | Mpa | Mpa | Length*width*height | ||||
(Ratio%) | |||||||||||||||||
Testing standard | GB/T 8813-2008 | GB/T 9641-1988 | GB/T 1455-2008 | GB/T 8812.2-2007 | GB/T 10799-2008 | GB/T 8813-2008 | GB/T 8811-2008 | ||||||||||
32 | FF32 | 0.32 | 14 | 0.66 | 28 | 3.8 | 0.28 | 7.6 | 0.86 | 31 | 22 | 99 | 0.27 | 11 | 0.22 | 0.2 | 0.46 |
FU30 | 0.42 | 20 | 0.56 | 39 | 0.69 | — | — | 1 | 31 | 30 | — | 0.35 | 16 | 0.22 | 0.23 | 0.49 | |
40 | FC40 | 0.6 | 34 | 0.9 | 54 | 1.7 | 0.4 | 19 | 1.3 | 55 | 15 | — | 0.4 | 17 | — | — | — |
FU40 | 0.72 | 29 | 1.2 | 51 | 3.4 | — | — | 1.7 | 58 | 33 | — | 0.52 | 24 | 0.22 | 0.24 | 0.59 | |
52 | FC52 | 0.9 | 41 | 1.2 | 73 | 1.9 | 0.73 | 27 | 1.6 | 70 | 19 | 99 | 0.62 | 28 | 0.15 | 0.15 | 0.32 |
FM52 | 0.9 | 51 | 1.3 | 81 | 1.2 | 1 | 26 | 1.5 | 65 | 15 | 97 | 0.5 | 24 | 0.2 | 0.2 | 0.34 | |
FF52 | 1 | 43 | 1.5 | 77 | 3.1 | 0.9 | 24 | 2.1 | 76 | 22 | 99 | 0.6 | 27 | 0.28 | 0.3 | 0.46 | |
75 | FC72 | 1.4 | 59 | 1.8 | 101 | 2.3 | 1.2 | 40 | 2 | 92 | 13 | 99 | 0.9 | 43 | 0.21 | 0.22 | 0.35 |
FF75 | 1.8 | 72 | 2.4 | 113 | 3.6 | 1.6 | 45 | 3.4 | 117 | 20 | 98 | 1.1 | 49 | 0.2 | 0.16 | 0.48 | |
FU75 | 1.7 | 75 | 2.2 | 89 | 3.8 | 1.2 | 37 | 3.3 | 105 | 23 | — | 1.1 | 48 | 0.19 | 0.24 | 0.33 | |
110 | FF110 | 3.2 | 138 | 3.9 | 200 | 2.7 | 2 | 63 | 5.5 | 195 | 19 | 98 | 1.7 | 77 | 0.19 | 0.19 | 0.4 |
FU110 | 2.2 | 93 | 3.3 | 160 | 3.6 | 2.2 | 63 | 4.5 | 143 | 21 | — | 1.4 | 62 | 0.23 | 0.21 | 0.48 | |
200 | FF200 | 8.5 | 317 | 7.5 | 410 | 2.4 | — | — | 13 | 449 | 22 | 99 | 3.8 | 141 | 0.44 | 0.41 | 0.54 |